Multistimuli-Responsive PNIPAM-Based Double Cross-Linked Conductive Hydrogel with Self-Recovery Ability for Ionic...

Multistimuli-responsive conductive hydrogels have been appealing candidates for multifunctional ionic skin. However, the fabrication of the multistimuli-responsive conductive hydrogels with satisfactory mechanical property to meet the practical applications is still a great challenge. In this study, a novel poly(N-isopropylacrylamide-co-sodium acrylate)/alginate/hectorite clay Laponite XLS (PNIPAM-SA/ALG/XLS) double cross-linked hydrogel with excellent mechanical property, self-recovery ability, temperature/pH-responsive ability, and strain/temperature-sensitive conductivity was fabricated. The PNSAX hydrogel possessed a moderate tensile strength of 290 kPa at a large elongation rate of 1120% and an excellent compression strength of 2.72 MPa at 90%. The hydrogel also possessed excellent mechanical repeatability and self-recovery ability. Thus, the hydrogel could withstand repetitive deformations for long time periods. Additionally, the hydrogel could change its transparency and volume once at a temperature of 44 °C and change its volume at different pHs. Thus, the visual temperature/pH-responsive ability allowed the hydrogel to qualitatively harvest environmental information. Moreover, the hydrogel possessed an excellent conductivity of 0.43 S/m, and the hydrogel could transform large/subtle deformation and temperature information into electrical signal change. Thus, the ultrafast strain/temperature-sensitive conductivity allowed the hydrogel to quantitatively detect large/small-scale human motions as well as environmental temperature. A cytotoxicity test confirmed the good cytocompatibility. Taken together, the hydrogel was suitable for human motion detecting and environmental information harvesting for long time periods. Therefore, the hydrogel has a great application potential as a multifunctional ionic skin and smart sensor.