Interface Reversible Electric Field Regulated by Amphoteric Charged Protein-Based Coating Toward High-Rate and Robust...

Metallic interface engineering is a promising strategy to stabilize Zn anode via promoting Zn²⁺ uniform deposition. However, strong interactions between the coating and Zn²⁺ and sluggish transport of Zn²⁺ lead to high anodic polarization. Here, we present a bio-inspired silk fibroin (SF) coating with amphoteric charges to construct an interface reversible electric field, which manipulates the transfer kinetics of Zn²⁺ and reduces anodic polarization. The alternating positively and negatively charged surface as a build-in driving force can expedite and homogenize Zn²⁺ flux via the interplay between the charged coating and adsorbed ions, endowing the Zn-SF anode with low polarization voltage and stable plating/stripping. Experimental analyses with theoretical calculations suggest that SF can facilitate the desolvation of [Zn(H₂O)₆]²⁺ and provide nucleation sites for uniform deposition. Consequently, the Zn-SF anode delivers a high-rate performance with low voltage polarization (83 mV at 20 mA cm^-2) and excellent stability (1500 h at 1 mA cm^-2; 500 h at 10 mA cm^-2), realizing exceptional cumulative capacity of 2.5 Ah cm^-2. The full cell coupled with Zn_xV₂O₅·nH₂O (ZnVO) cathode achieves specific energy of ~ 270.5/150.6 Wh kg^-1 (at 0.5/10 A g^-1) with ~ 99.8% Coulombic efficiency and retains ~ 80.3% (at 5.0 A g^-1) after 3000 cycles.