Utilization of Lead Slag as In Situ Iron Source for Arsenic Removal by Forming Iron Arsenate

In situ treatment of acidic arsenic-containing wastewater from the non-ferrous metal smelting industry has been a great challenge for cleaner production in smelters. Scorodite and iron arsenate have been proved to be good arsenic-fixing minerals; thus, we used lead slag as an iron source to remove arsenic from wastewater by forming iron arsenate and scorodite. As the main contaminant in wastewater, As(III) was oxidized to As(V) by H₂O₂, which was further mineralized to low-crystalline iron arsenate by Fe(III) and Fe(II) released by lead slag (in situ generated). The calcium ions released from the dissolved lead slag combined with sulfate to form well-crystallized gypsum, which co-precipitated with iron arsenate and provided attachment sites for iron arsenate. In addition, a silicate colloid was generated from dissolved silicate minerals wrapped around the As-bearing precipitate particles, which reduced the arsenic-leaching toxicity. A 99.95% removal efficiency of arsenic with initial concentration of 6500 mg/L was reached when the solid-liquid ratio was 1:10 and after 12 h of reaction at room temperature. Moreover, the leaching toxicity of As-bearing precipitate was 3.36 mg/L (As) and 2.93 mg/L (Pb), lower than the leaching threshold (5 mg/L). This work can promote the joint treatment of slag and wastewater in smelters, which is conducive to the long-term development of resource utilization and clean production.