Experimental Study on the Mechanical Properties of Diatomite-Modified Coastal Cement Soil

Diatomite is a non-metallic mineral resource rich in SiO₂, which can be used to modify coastal cement soil. In order to explore the mechanical modification effect of diatomite on coastal cement soil at the age of 7 days, based on coastal cement soil with cement content of 5% (mass fraction), diatomite of 0%, 5%, 10%, 15% and 20% (mass fraction) was mixed for modification. Through the unconfined compressive strength test, the triaxial unconsolidated undrained test, backscattered electron imaging (BSE), and energy-dispersive spectroscopy (EDS) technology, the influence of diatomite content and confining pressure on the peak strength of modified coastal cement soil was explored. The empirical formula between the peak strength of the DE specimen and the content of diatomite and confining pressure was established by curve fitting, and the fitting effect was ideal. When diatomite was mixed with coastal cement soil, the optimal dosage of diatomite was 5% from the perspective of mechanical properties and economic benefits of the maximum growth rate of compression and shear. The unconfined compressive strength test showed that the peak strength and elastic modulus of the modified coastal cement soil with 5% diatomite content were 37% and 57% higher than those of cement soil, respectively. The triaxial unconsolidated undrained test showed that the internal friction angle of the modified coastal cement soil was stable at about 30°, and cohesion of DE-5, DE-10, DE-15, and DE-20 increased by 28%, 48%, 78%, and 97%, respectively, compared to cement soil. The microscopic test found that the pore distribution of modified coastal cement soil is closely related to the strength change. The results show that the addition of diatomite can effectively improve the mechanical properties of soil-cement.