Ti₃C₂T_x-Modified PEDOT:PSS Hole-Transport Layer for Inverted Perovskite Solar Cells

PSS is a commonly used hole-transport layer (HTL) in inverted perovskite solar cells (PSCs) due to its compatibility with low-temperature solution processing. However, it possesses lower conductivity than other conductive polymers and metal oxides, along with surface defects, limiting its photovoltaic performance. In this study, we introduced two-dimensional Ti₃C₂T_x (MXene) as an additive in the PEDOT:PSS HTL with varying doping concentrations (i.e., 0, 0.03, 0.05, and 0.1 wt.%) to tune the electrical conductivity of PEDOT:PSS and to modify the properties of the perovskite film atop it. We noted that the grain size of the CH₃NH₃PbI₃ (MAPI₃) perovskite layer grown over an optimal concentration of MXene (0.03 wt.%)-doped PEDOT:PSS increased from 250 nm to 400 nm, reducing charge recombination due to fewer grain boundaries. Ultraviolet photoelectron spectroscopy (UPS) revealed increased work function (WF) from 4.43 eV to 4.99 eV with 0.03 wt.% MXene doping, making the extraction of holes easier due to a more favorable energy level alignment with the perovskite. Quantum chemical investigations based on density functional theory (DFT) were conducted at the ωB97XD/6-311++G(d,p) level of theory to provide more insight into the stability, bonding nature, and optoelectronic properties of the PEDOT:PSS-MXene system. The theoretical investigations revealed that the doping of PEDOT:PSS with Ti₃C₂T_x could cause a significant effect on the electronic properties of the HTL, as experimentally demonstrated by an increase in the electrical conductivity. Finally, the inverted PSCs employing 0.03 wt.% MXene-doped PEDOT:PSS showed an average power conversion efficiency (PCE) of 15.1%, up from 12.5% for a reference PSC employing a pristine PEDOT:PSS HTL. The champion device with a 0.03 wt.% MXene-PEDOT:PSS HTL achieved 15.5% PCE.