Synthesis of Nanosilica for the Removal of Multicomponent Cd²⁺ and Cu²⁺ from Synthetic Water: An Experimental and...

Copper and cadmium ions are among the top 120 hazardous chemicals listed by the Agency for Toxic Substances and Disease Registry (ATSDR) that can bind to organic and inorganic chemicals. Silica is one of the most abundant oxides that can limit the transport of these chemicals into water resources. Limited work has focused on assessing the applicability of nanosilica for the removal of multicomponent metal ions and studying their interaction on the surface of this adsorbent. Therefore, this study focuses on utilizing a nanosilica for the adsorption of Cd²⁺ and Cu²⁺ from water. Experimental work on the single- and multi-component adsorption of these ions was conducted and supported with theoretical interpretations. The nanosilica was characterized by its surface area, morphology, crystallinity, and functional groups. The BET surface area was 307.64 m²/g with a total pore volume of 4.95×10-3 cm³/g. The SEM showed an irregular amorphous shape with slits and cavities. Several Si-O-Si and hydroxyl groups were noticed on the surface of the silica. The single isotherm experiment showed that Cd²⁺ has a higher uptake (72.13 mg/g) than Cu²⁺ (29.28 mg/g). The multicomponent adsorption equilibrium shows an affinity for Cd²⁺ on the surface. This affinity decreases with increasing Cu²⁺ equilibrium concentration due to the higher isosteric heat from the interaction between Cd and the surface. The experimental data were modeled using isotherms for the single adsorption, with the Freundlich and the non-modified competitive Langmuir models showing the best fit. The molecular dynamics simulations support the experimental data where Cd²⁺ shows a multilayer surface coverage. This study provides insight into utilizing nanosilica for removing heavy metals from water.