Compression Performance and Failure Analysis of 3D-Printed Carbon Fiber/PLA Composite TPMS Lattice Structures

Triply periodic minimum surface (TPMS)-based lattice structures have gained interest for their outstanding capacity to absorb energy, their high load-bearing capacity, and their high surface-to-volume ratio. This study considered three TPMS cell topologies, including Diamond, Gyroid, and Primitive. The FDM process was used to print the lattice structures with two materials: pure polylactic acid (PLA) and carbon fiber-reinforced PLA (PLA + CF). The influence of carbon fiber (CF) incorporation, unit cell type (topologies) and size, and relative density (RD) on mechanical properties and failure patterns were explored comprehensively under uniaxial compression testing. The results demonstrate a change in the compressive modulus (0.09 to 0.47 GPa), compressive strength (2.98 to 13.89 MPa), and specific energy absorption (SEA) (0.14 MJ/m³/g to 0.58 MJ/m³/g) due to the influence of CF incorporation, cell type and size, and RD. Results indicate that the Diamond structure outperformed both Primitive and Gyroid structures in terms of compressive modulus and strength, and SEA. All the CF-based TPMS structures showed a higher compressive modulus. Compressive strength and energy absorption capacity were both slightly enhanced in most PLA + CF-based Diamond structures. On the contrary, Gyroid and Primitive structures showed better performance for pure PLA-based structures in terms of compression strength and specific absorption energy.