Biocompatible carboxymethyl chitosan-modified glass ionomer cement with enhanced mechanical and anti-bacterial...

Due to the potential adverse effects of conventional dental cements, the demand for biocompatible cements have grown tremendously in the field of dentistry. In this respect, Glass ionomer cements (GICs) are being developed by different researchers. However, low mechanical strength of GIC make them unsuitable for application in high-stress areas. Thus, numerous initiatives to improve mechanical performance have been attempted till date including incorporation of reinforcing fillers. Novelty of the study lies in using carboxymethyl chitosan (CMC) to develop a biocompatible dental cement (DC/CMC-m-GP), which would have enhanced mechanical strength due to greater interaction of CMC with the particles of GIC and better cyto-compatibility due to its cell-proliferation activity. The mechanical strength, acid erosion and fluoride release of DC/CMC-m-GP were studied and compared with control dental cement (DC/Control). DC/CMC-m-GP shows compressive strength of 157.45 M Pa and flexural strength of 18.76 M Pa which was higher as compared to DC/Control. The morphology of the GICs were studied through FESEM. Anti-microbial activity of DC/CMC-m-GP was studied by Agar disc-diffusion method and biofilm assay against S. mutans, which shows that DC/CMC-m-GP inhibits bacterial adhesion on its surface. MTT assay infers that DC/CMC-m-GP was non-cytotoxic and did not affect the cell viability significantly.