Efficient Photocatalytic Hydrogen Production over NiS-Modified Cadmium and Manganese Sulfide Solid Solutions

In this work, new photocatalysts based on Cd_1-xMn_xS sulfide solid solutions were synthesized by varying the fraction of MnS (x = 0.4, 0.6, and 0.8) and the hydrothermal treatment temperature (T = 100, 120, 140, and 160 °C). The active samples were modified with Pt and NiS co-catalysts. Characterization was performed using various methods, including XRD, XPS, HR TEM, and UV-vis spectroscopy. The photocatalytic activity was tested in hydrogen evolution from aqueous solutions of Na₂S/Na₂SO₃ and glucose under visible light (425 nm). When studying the process of hydrogen evolution using an equimolar mixture of Na₂S/Na₂SO₃ as a sacrificial agent, the photocatalysts Cd_0.5Mn_0.5S/Mn(OH)₂ (T = 120 °C) and Cd_0.4Mn_0.6S (T = 160 °C) demonstrated the highest activity among the non-modified solid solutions. The deposition of NiS co-catalyst led to a significant increase in activity. The best activity in the case of the modified samples was shown by 0.5 wt.% NiS/Cd_0.5Mn_0.5S (T = 120 °C) at the extraordinary level of 34.2 mmol g^-1 h^-1 (AQE 14.4%) for the Na₂S/Na₂SO₃ solution and 4.6 mmol g^-1 h^-1 (AQE 2.9%) for the glucose solution. The nickel-containing samples possessed a high stability in solutions of both sodium sulfide/sulfite and glucose. Thus, nickel sulfide is considered an alternative to depositing precious metals, which is attractive from an economic point of view. It worth noting that the process of photocatalytic hydrogen evolution from sugar solutions by adding samples based on Cd_1-xMn_xS has not been studied before.