Cu Nanowires and Nanoporous Ag Matrix Fabricated through Directional Solidification and Selective Dissolution of...

Cu nanowires and a nanoporous Ag matrix were fabricated through directional solidification and selective dissolution of Ag-Cu eutectic alloys. Ag-39.9at.%Cu eutectic alloys were directionally solidified at growth rates of 14, 25, and 34 μm/s at a temperature gradient of 10 K/cm. The Cu phase in the Ag matrix gradually changed from lamellar to fibrous with an increase in the growth rate. The Ag matrix phase was selectively dissolved, and Cu nanowires of 300-600 nm in diameter and tens of microns in length were prepared in 0.1 M borate buffer with a pH of 9.18 at a constant potential of 0.7 V (vs. SCE). The nanoporous Ag matrix was fabricated through selective dissolution of Cu fiber phase in 0.1 M acetate buffer with a pH of 6.0 at a constant potential of 0.5 V (vs. SCE). The diameter of Ag pores decreased with increasing growth rate. The diameter and depth of Ag pores increased when corrosion time was extended. The depth of the pores was 30 μm after 12 h.