The Structural Evolution and Mechanical Properties of Semi-Aromatic Polyamide 12T after Stretching

The development of semi-aromatic polyamides with excellent mechanical properties has always been a popular research avenue. In this work, the semi-aromatic polyamide 12T (PA12T) with the maximum tensile strength of 465.5 MPa was prepared after stretching at 210 °C 4.6 times. Wide-angle X-ray diffraction (WAXD) and small-angle X-ray scattering (SAXS) were used to characterize the structural evolution of semi-aromatic polyamide 12T (PA12T) after stretching at different stretching temperatures and stretching ratios. The formation mechanism of this change in mechanical properties was investigated from different aspects of the aggregated structure such as crystal morphology, crystal orientation and crystallinity. The relevant characterization results show that the crystal structure, crystal orientation and crystallinity of PA12T were the highest when the sample was pre-stretched at 210 °C, which is crucial for improving the mechanical properties of PA12T. These findings will provide important guidance for the preparation of polymer materials with excellent mechanical properties.