Numerical Investigation of the Elastic Properties of Polypropylene/Ultra High Molecular Weight Polyethylene Fiber

Jong-Hwan Yun1, Yu-Jae Jeon2, Min-Soo Kang3

  • 1Mobility Materials-Parts-Equipment Center, Kongju National University, Gongju-si 32588, Korea.

Polymers
|November 26, 2022
PubMed

Keywords:
aspect ratiocompositepolypropyleneultrahigh molecular weight polyethylenevolume fraction

More Related Videos

Author Spotlight: Enhancing Fiber Composite Laminate Quality with the Wet Hand Lay-Up/Vacuum Bag Process09:54

Author Spotlight: Enhancing Fiber Composite Laminate Quality with the Wet Hand Lay-Up/Vacuum Bag Process

Published on: June 30, 2023

2.3K
Cutting Procedures, Tensile Testing, and Ageing of Flexible Unidirectional Composite Laminates07:53

Cutting Procedures, Tensile Testing, and Ageing of Flexible Unidirectional Composite Laminates

Published on: April 27, 2019

8.3K

Related Concept Videos

Bending of Members Made of Several Materials01:08

Bending of Members Made of Several Materials

In analyzing a structural member composed of two different materials with identical cross-sectional areas, it is crucial to understand how their distinct elastic properties affect the member's response under load. The analysis involves assessing stress and strain distributions using the transformed section concept, which accounts for variations in material properties.
Hooke's Law determines stress in each material, stating that stress is proportional to strain but varies due to each...
248
Hooke's Law01:26

Hooke's Law

Hooke's law, a pivotal principle in material science, establishes that the strain a material undergoes is directly proportional to the applied stress, defined by a factor called the modulus of elasticity or Young's modulus.
517
Members Made of Elastoplastic Material01:19

Members Made of Elastoplastic Material

The behavior of elastoplastic materials under bending stresses, particularly in structural members with rectangular cross-sections, is crucial for predicting material responses and understanding failure modes. Initially, when a bending moment is applied, the stress distribution across the section follows Hooke's Law and is linear and elastic. This distribution means the stress increases from the neutral axis to the maximum at the outer fibers, up to the elastic limit.
As the bending moment...
132
Relation between Poisson's ratio, Modulus of Elasticity and Modulus of Rigidity01:15

Relation between Poisson's ratio, Modulus of Elasticity and Modulus of Rigidity

Deformation occurs in axial and transverse directions when an axial load is applied to a slender bar. This deformation impacts the cubic element within the bar, transforming it into either a rectangular parallelepiped or a rhombus, contingent on its orientation. This transformation process induces shearing strain. Axial loading elicits both shearing and normal strains. Applying an axial load instigates equal normal and shearing stresses on elements oriented at a 45° angle to the load axis.
313
Molecular Weight of Step-Growth Polymers01:08

Molecular Weight of Step-Growth Polymers

Step growth polymerization involves bi or multifunctional monomers. Bifunctional monomers react to form linear step growth polymers, whereas multifunctional monomers react to form non-linear or branched polymers.
As the step-growth polymerization involves step-wise condensation of monomers, the molecular weight also builds up eventually. Consequently, high molecular weight polymers are obtained at the late stages of the polymerization, where 99% of monomers have been consumed.
The extent of the...
2.3K
Polymers: Molecular Weight Distribution01:10

Polymers: Molecular Weight Distribution

For any given polymer, the weight average molecular weight (Mw) is higher than, if not equal to, the number average molecular weight (Mn). The only situation in which the weight average molecular weight and the number average molecular weight are equal is when a polymer consists only of chains with equal molecular weight. However, this never happens in a synthetic polymer, since it is difficult to control the polymerization process up to a molecular level with accuracy to a hundred percent.
3.6K