Cerium oxide: synthesis, brief characterization, and optimization of the photocatalytic activity against...

Water pollution by antibiotics is a global crisis, and its risk is critically more severe due to the explosive use of these drug compounds. A critical effective removal method to diminish this risk is heterogeneous photocatalysis and optimizing the conditions to reach higher mineralization efficiency. CeO₂ anoparticles (NPs) were synthesized and characterized by X-ray diffraction (XRD), UV-Vis diffuse reflection spectroscopy (DRS), and Fourier transform infrared spectroscopy (FTIR) techniques. A cubic structural crystallite phase was detected that had crystallite sizes of 17.9 and 16.7 nm estimated by the Scherrer and Williamson-Hall models. A typical FTIR absorption band for the Ce-O stretching absorption has appeared at 554 cm^-1. Based on DRS data and the Kubelka-Munk and Tauc models, Eg values of 2.80, 3.06, 3.12, and 3.13 eV were obtained for n-values of 1/2, 2, 3/2, and 3, respectively. pHpzc of CeO₂ NPs was about 5.7. The direct photolysis and surface adsorption processes have no critical role in phenazopyridine (PP) removal by appearing with 2.7 and 6.7% removal efficiencies, respectively. Due to the highest photocatalytic activity of CeO₂ NPs toward PP, the effects of the critical operating variable on the activity were evaluated, and the optimal conditions were as catalyst dose, 0.7 g/L; pH, 6; irradiation time, 90 min; and C_PP, 20 ppm. The Hinshelwood kinetics equation plot was y =  - 6.6442 - 0.4677x (r² = 0.9296), in which its slope as the rate constant of the photodegradation process was 0.4677 min^-1 (corresponding to a t_1/2 value of 1.48 min).