Porous hydroxyapatite scaffold orchestrated with bioactive coatings for rapid bone repair

Current bioceramic scaffolds for critical-size bone defects are still facing various challenges such as the poor capability of self-resorption, vascularization and osteogenesis. Herein, a composite scaffold (HOD) is fabricated by integrating bioactive coatings of konjac glucomannan (KGM) and deferoxamine (DFO) into porous hydroxyapatite scaffold (HA), where KGM coating induces the self-resorption of HOD after implanting and DFO promoted the vascularization at the defected bone. Porous HA scaffolds with 200-400 μm of pore sizes were prepared and these bioactive coatings were successfully deposited on the scaffold, which was confirmed by SEM. MC3T3-E1 cells could be tightly attached to the pore wall of HOD and the obvious osteogenic differentiation was clearly displayed after 14 days of co-culture. Besides, HOD displayed the potential of promoting the vascularization of HUVECs. Importantly, the accelerated degradation of HOD was observed in a macrophage-associated acidic medium, which led to the self-resorption of HOD in vivo. Micro-CT images showed that HOD was gradually replaced by newly formed bone, achieving a balance between the new bone formation and the scaffold degradation. The rapid bone repairing of the femoral defects in rats was displayed for HOD in comparison to the HA scaffold. Moreover, the therapeutic mechanism of HOD was highly associated with promoted osteogenesis and vascularization. Collectively, the porous ceramic scaffold orchestrated with bioactive coatings may be a promising strategy for repairing of the large bone defect.