Solvent-free synthesis of high-performance polyurethane elastomer based on low-molecular-weight alkali lignin

Using cheap and green lignin as a partial substitute for petroleum-based polyols is highly attractive for sustainable development of polyurethane elastomers (LPUes). However, the traditional synthesis process of LPUes inevitably uses toxic solvents that are difficult to remove or carcinogenic. Here, we reported a solvent-free synthesis method to prepare lignin-containing polyurethane elastomers (SF-LPUes) with high strength, high toughness and high elasticity. Most of the hydroxyl groups of lignin reacted with isocyanates to form a strong chemical cross-linking network, while the unreacted ones formed a dynamic hydrogen bond network with polyurethane matrix, contributing to the in-situ formation of lignin nanoparticles to build a nano-micro phase separation structure. Consequently, a dual-crosslinking network structure was formed and endowed SF-LPUes with excellent mechanical properties. Especially, the SF-LPUes prepared from low molecular alkali lignin possessed a tensile strength as high as 38.2 MPa, a maximum elongation at break of 1108 %, and an elastic recovery ratio of up to 98.7 %. Moreover, SF-LPUes showed impressing reprocessing performance and aging resistance. This work provides an industrial application prospect for the synthesis of lignin-containing polyurethane elastomers via a solvent-free synthesis process.