Force profile assessment of direct-printed aligners versus thermoformed aligners and the effects of non-engaged
Evan Hertan1, Julie McCray1, Brent Bankhead1
1Department of Orthodontics, Saint Louis University, 3320 Rutger Street, Saint Louis, MO, 63104, USA.
Background:
The purpose of the study was to measure the forces delivered by direct-printed aligners (DPA) in the vertical dimension and compare the force profile with traditional thermoformed aligners (TFA) and to investigate the impact of non-engaged surface patterns to the properties of DPA and TFA.
Methods:
A force-measuring appliance was fabricated capable of displacing the aligner in 0.10 mm increments and measuring the resultant force. Polyethylene terephthalate glycol (ATMOS 0.030″ American Orthodontics) and TC-85DAC resin (Graphy Inc) were used to create TFA and DPA, respectively. Aligners were temperature-controlled prior to and during testing to simulate the oral environment. The resultant forces from displacements ranging from 0.10 to 0.30 mm were measured.
Results:
At intraoral temperatures, DPA demonstrated significantly less force than TFA. TFA demonstrated a substantial statistically significant increase in force with each 0.10 mm increase in vertical displacement. DPA demonstrated a much more consistent force profile across the range of displacements. The effects of surface patterns in both DPA and TFA were generally a decrease in force. Statistical significance of surface patterns was detected for TFA at displacements of 0.30 mm and greater and significant for DPA only at a displacement of 0.10 mm. Surface patterns in both DPA and the TFA did not show any statistical difference when assessing force proprieties.
Conclusions:
Forces delivered by aligners in the vertical dimension by DPA are more consistent and of lower magnitude than those of TFA aligners. Surface patterns were not capable of altering the force properties of both DPA and TFA.