Nano-α-Fe₂ O₃ for enhanced denitrification in a heterotrophic/biofilm-electrode autotrophic denitrification reactor

In this study, a heterotrophic/biofilm-electrode autotrophic denitrification reactor (HAD-BER) was constructed and nano-ɑ-Fe₂ O₃ was coated on granular activated carbon (GAC) as a third electrode to enhance the nitrate removal performance. The introduction of nano-ɑ-Fe₂ O₃ could stimulate microorganisms to secrete more extracellular polymeric substances (EPS), accelerating the electron transfer. Moreover, more denitrification bacteria were enriched on the particle electrodes, especially Pseudomonas and Thermomonas, which played a significant role in denitrification. The denitrification performance at different COD/N ratios (0.65-3.23) and current intensities (0-150 mA) was investigated in depth. When the nitrate concentration of the influent was 60 mg/L, nitrate was almost completely removed at the optimal current intensity (60 mA) and COD/N ratio (1.29). At the same time, there was almost no nitrite (<0.10 mg/L) and ammonia nitrogen (0 mg/L) accumulation in the effluent. This study provided a new direction for the advancement of HAD-BER and accelerated its implementation. PRACTITIONER POINTS: By introducing nano-a-Fe2O3 into HAD-BER, more denitrification bacteria were enriched on the particle electrodes. The increased contents of polysaccharide and protein content could accelerate the electron transfer. Almost completely denitrification could be achieved at current = 60 mA and COD/N = 1.29. The study provided a new direction for the further development of HAD-BERs.