Effect of surface structure on the antithrombogenicity performance of poly(-caprolactone)-cellulose acetate...

Small-diameter artificial blood vessels have always faced the problem of thrombosis. In this research, three types of poly(-caprolactone)-cellulose acetate (PCL-CA) composite nanofiber membranes were prepared by various collectors to make into a tubular scaffold with a 4.5-mm diameter. The collector consisted of two sizes of stainless steel wire mesh large-mesh (LM) and small-mesh (SM), respectively. There is also a random flat (RF) that acts as the third type collector. The nanofiber membrane's surface structure mimicked the collectors' surface morphology, they named LM, SM and RF scaffolds. The water contact angles of RF and LM scaffolds are 126.5° and 105.5°, and the distinct square-groove construction greatly improves the contact angle of LM. The tubular scaffolds' radial mechanical property test demonstrated that the large-mesh (LM) tubular scaffold enhanced the strain and tensile strength; the tensile strength and strain are 30 % and 148 % higher than that of the random-flat (RF) tubular scaffold, respectively. The suture retention strength value of the LM tubular scaffold was 103 % higher than that of the RF tubular scaffold. The cytotoxicity and antithrombogenicity performance were also evaluated, the LM tubular scaffold has 88 % cell viability, and the 5-min blood coagulation index (BCI) value was 89 %, which is much higher than other tubular scaffolds. The findings indicate that changing the tubular scaffold's surface morphology cannot only enhance the mechanical and hydrophilic properties but also increase cell survival and antithrombogenicity performance. Thus, the development of a small-diameter artificial blood vessel will be a big step toward solving the problem on thrombosis. Furthermore, artificial blood vessel is expected to be a candidate material for biomedical applications.