Analysis of the Real Performance of Crumb-Rubber-Modified Asphalt Mixtures

Francisco Javier Sierra-Carrillo de Albornoz1, Fernando Moreno-Navarro2, María Del Carmen Rubio-Gámez2

  • 1Consejería de Infraestructuras, Fomento y Ordenación del Territorio Junta de Andalucía, Avda. Joaquina Eguaras 2, 18071 Granada, Spain.

Materials (Basel, Switzerland)
|December 11, 2022
PubMed

Keywords:
asphaltcrackingcrumb rubberfield performancestiffness

More Related Videos

Advanced Self-Healing Asphalt Reinforced by Graphene Structures: An Atomistic Insight08:03

Advanced Self-Healing Asphalt Reinforced by Graphene Structures: An Atomistic Insight

Published on: May 31, 2022

4.6K
The Preparation and Properties of Thermo-reversibly Cross-linked Rubber Via Diels-Alder Chemistry07:02

The Preparation and Properties of Thermo-reversibly Cross-linked Rubber Via Diels-Alder Chemistry

Published on: August 25, 2016

13.8K

Related Concept Videos

Toughness and Hardness of Aggregate01:22

Toughness and Hardness of Aggregate

Toughness and hardness are critical properties of aggregate materials used in concrete, particularly on pavement surfaces and industrial flooring subjected to heavy loads. Toughness is defined as the aggregate's resistance to failure by impact and is measured by the aggregate impact value (AIV). For this, the aggregate impact value test is performed, wherein the impact is delivered by a standard hammer, which falls freely under its own weight onto the aggregates. The aggregates fragment in...
313
Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...
177
Abrasion Resistance of Concrete01:23

Abrasion Resistance of Concrete

Abrasion resistance is an essential characteristic of concrete that determines its durability and longevity under various wear conditions. Concrete surfaces are vulnerable to different types of abrasion. For instance, surfaces may wear down due to the constant movement of vehicles or be eroded by solids carried in water, as seen in concrete canal linings. Specific tests are conducted to measure the abrasion resistance of concrete.
One such test is the revolving disc test, where three plates...
177
Aggregate Cement Ratio01:21

Aggregate Cement Ratio

The Aggregate Cement ratio refers to the weight of aggregate divided by the weight of cement in a concrete mix. Altering this ratio has profound effects on the concrete's properties. This ratio plays a pivotal role in determining the strength, workability, and durability of concrete. When the Aggregate Cement ratio is higher, the mix is leaner, meaning it has less cement paste to lubricate the aggregate, potentially making the concrete less workable. Such mixes, known as lean, enhance the...
299
Design Example: Managing Concrete Workability01:14

Design Example: Managing Concrete Workability

This example deals with managing the workability of concrete for a raft foundation project under hot weather conditions. Workability is crucial for ensuring the concrete is easy to place, compact, and finish. In this scenario, a slump test — a common method to measure the workability of fresh concrete — initially indicated low workability. This was attributed to the rapid water loss from the concrete mix, exacerbated by the high temperatures causing the course aggregates to heat up.
109
Slump Test01:20

Slump Test

The slump test is a widely used method to measure the workability of concrete. It employs a 12-inch high truncated cone mold that tapers from eight inches at the base to four inches at the top. Before testing, the mold is securely attached to a flat base and dampened.
Concrete is poured into the mold in three layers to conduct the test. Each layer is compacted 25 times with a steel tamping rod, which has a five-eighths-inch diameter and a rounded end, to ensure even distribution and eliminate...