Core-Shell Carbon Nanofibers@Ni(OH)2/NiO Composites for High-Performance Asymmetric Supercapacitors
Peizhi Fan1, Lan Xu1
1National Engineering Laboratory for Modern Silk, College of Textile and Engineering, Soochow University, Suzhou 215123, China.
Abstract:
The application of transition metal oxides/hydroxides in energy storage has long been studied by researchers. In this paper, the core-shell CNFs@Ni(OH)2/NiO composite electrodes were prepared by calcining carbon nanofibers (CNFs) coated with Ni(OH)2 under an N2 atmosphere, in which NiO was generated by the thermal decomposition of Ni(OH)2. After low-temperature carbonization at 200 °C, 250 °C and 300 °C for 1 h, Ni(OH)2 or/and NiO existed on the surface of CNFs to form the core-shell composite CNFs@Ni(OH)2/NiO-X (X = 200, 250, 300), in which CNFs@Ni(OH)2/NiO-250 had the optimal electrochemical properties due to the coexistence of Ni(OH)2 and NiO. Its specific capacitance could reach 695 F g-1 at 1 A g-1, and it still had 74% capacitance retention and 88% coulomb efficiency after 2000 cycles at 5 A g-1. Additionally, the asymmetric supercapacitor (ASC) assembled from CNFs@Ni(OH)2/NiO-250 had excellent energy storage performance with a maximum power density of 4000 W kg-1 and a maximum functional capacity density of 16.56 Wh kg-1.
More Related Videos
12:00Evaluating the Electrochemical Properties of Supercapacitors using the Three-Electrode System
Published on: January 7, 2022
08:59Synthesizing a Gel Polymer Electrolyte for Supercapacitors, Assembling a Supercapacitor Using a Coin Cell, and Measuring Gel Electrolyte Performance
Published on: November 30, 2022