Assessment of the Synergetic Performance of Nanostructured CeO₂-SnO₂/Al₂O₃ Mixed Oxides on Automobile Exhaust Control

In order to control diesel exhaust emission, CeO₂-SnO₂/Al₂O₃ (CTA) mixed oxides were prepared and coated on perforated stainless steel (SS) filter plates, and the catalytic activities were analyzed in this work. The CeO₂-SnO₂ (different compositions of Ce/Sn-2:8; 1:1; 8:2) composites and Al₂O₃ were prepared separately via a co-precipitation approach, and CeO₂-SnO₂/Al₂O₃ (CTA) mixed oxides were attained by mechanical mixing of 75 wt% CeO₂-SnO₂ composites with 25 wt% Al₂O₃. X-ray diffraction (XRD) and Raman spectroscopy were performed for all three CeO₂-SnO₂/Al₂O₃ (CTA) mixed oxides; the CeO₂-SnO₂/Al₂O₃ (Ce/Sn-1:1) sample confirmed the presence of cubic and tetragonal mixed faces, which enhances the redox nature (catalytic activities). Various characterizations such as high-resolution transmission electron microscopy (HRTEM), Brunauer-Emmett-Teller (BET) analysis, X-ray photoelectron spectroscopy (XPS), and a scanning electron microscope (SEM) were employed on CeO₂-SnO₂/Al₂O₃ (Ce/Sn-1:1) sample to investigate the structural, textural, compositional, and morphological properties. The CeO₂-SnO₂/Al₂O₃ (Ce/Sn-1:1) sample was coated on a perforated stainless steel (SS) filter plate via a simple, cost-effective, and novel method, and an exhaust emission test for various compression ratios (CR), injection pressure (IP), and load (L) was completed using an AVL Digas analyzer. The CeO₂-SnO₂/Al₂O₃ (Ce/Sn-1:1) sample, with a size of 10.22 nm and a high surface area of about 73 m² g^-1, exhibit appreciable catalytic properties.