Microstructures and Fatigue Properties of High-Strength Low-Alloy Steel Prepared through Submerged-Arc Additive...

Submerged arc additive manufacturing (SAAM) is a viable technique for manufacturing large and complex specialized parts used in structural applications. At present, manufacturing high-strength low-alloy steel T-branch pipe through SAAM has not been reported. This paper uses this technology to manufacture low-alloy structural steel parts. The microstructures of the samples were characterized, which revealed that they were mainly composed of polygonal ferrites. The tensile properties in the horizontal and vertical directions of deposits were studied. Results show that the horizontal tensile strength of deposits was quite close to the vertical one, while the elongation rate in the vertical direction was obviously lower than that in the horizontal direction. Fatigue results indicate that the strain fatigue limit of high-strength low-alloy steel samples in vertical direction was 0.24%. The fatigue fractures of fatigue samples of deposits showed multi-source crack initiation characteristics and the crack propagation regions exhibited typical fatigue striations, so the final instantaneous fracture region showed a ductile fracture. Fatigue performance is very important for the safe service of structural parts, but there is a lack of relevant research on this additive manufacturing part. The results of this paper may support the popularization of the SAAM for high-strength low-alloy steel T-branch pipe.