Enhanced Photoluminescence of Gd₃Al₄GaO₁₂: Cr³⁺ by Energy Transfers from Co-Doped Dy³

LEDs for plant lighting have attracted wide attention and phosphors with good stability and deep-red emission are urgently needed. Novel Cr3+ and Dy3+ co-doped Gd3Al4GaO12 garnet (GAGG) phosphors were successfully prepared through a conventional solid-state reaction. Using blue LEDs, a broadband deep-red emission at 650−850 nm was obtained due to the Cr3+ 4T2 → 4A2 transition. When the Cr3+ concentration was fixed to 0.1 mol, the crystal structure did not change with an increase in the Dy3+ doping concentration. The luminous intensity of the optimized GAGG:0.1Cr3+, 0.01Dy3+ was 1.4 times that of the single-doped GAGG:0.1Cr3+. Due to the energy transfer from Dy3+ to Cr3+, the internal quantum efficiency reached 86.7%. The energy transfer from Dy3+ to Cr3+ can be demonstrated through luminescence spectra and fluorescence decay. The excellent properties of the synthesized phosphor indicate promising applications in the agricultural industry.