Titanium Coated with Graphene and Niobium Pentoxide for Biomaterial Applications

Graphene and niobium oxide are used in biomaterial coatings. In this work, commercially pure titanium (cp Ti) was coated with graphene oxide (GO), niobium pentoxide (Nb₂O₅), and a mixture of both materials (NbGO) by the electrochemical deposition method. The surface morphology, roughness, wettability, and degradation of coated and uncoated samples were analyzed by scanning electron microscopy, interferometry, and contact angle. The results showed that the specimens coated with NbGO (cp Ti-NbGO) showed the highest surface roughness (Ra = 0.64 μm) and were hydrophobic. The contact (θ) angle between water and the surface of uncoated specimens (cp Ti), coated with GO (cp Ti-GO), coated with a mixture with GO and Nb₂O₅) (cp Ti-NbGO), and coated with Nb₂O₅ were 50.74°, 44.35°, 55.86°, and 100.35°, respectively. The electrochemical corrosion tests showed that coating with graphene oxide increased the corrosion resistance and coating with Nb₂O₅ decreased the corrosion resistance. The negative effect of the effect of Nb₂O₅ coating in corrosion resistance compensated for the release of Nb₂O₅, which helps osseointegration, increasing cell viability, and proliferation of osteoblasts. The NbGO coating may be a good way to combine the bactericidal effect of graphene oxide with the osseointegration effect of Nb₂O₅.