Establishing a high-performance anti-fouling PEI-ZIF-PAA membrane with improved Lewis acid-base interactions and hydrophilicity

Membrane fouling and the trade-off between membrane permeability and selectivity restrict the potential applications of membrane filtration for water treatment. ZIF-8 was found having great permeability and antibiofouling performance, but with issue on particle aggregation makes it difficult to achieve high ZIFs loading and fabricate a defect-free molecular sieving membrane in previous research. In this study, we formed a scalable antibiofouling surface with improved permeability and fouling resistance on a PEI-ZIF-PAA membrane using a layer-by-layer assembly technique. The synergistic effects of being sandwiched between two different polyelectrolyte layers with opposite charges endowed the ZIF nanoparticles with improved stability and scalability for membrane modification. The PEI-ZIF-PAA membrane exhibited a satisfactory water flux of 120.78 LMH, which was 46.97% higher than that of the pristine PES membrane. The normalized water flux loss was serious in the absence of ZIF-8, and the flux increased with the ZIF-8 concentration. Antifouling tests suggested that the PEI-ZIF-PAA membrane possessed good antifouling performance due to the much higher surface hydrophilicity and positive Lewis acid-base interactions with foulants. The HA rejection increased with the ZIF-8 concentration and reached a maximum of 92.1% in the presence of 1.00% (w/v) ZIF-8. The membrane regeneration was tested under physical and chemical cleaning with flux recovery rates of about 85% and 95%. XDLVO analysis showed that the total interaction energy between HA and the PEI-ZIF-8-PAA membrane was 26.45 mJ/m², and the superior antifouling performance was mainly attributed to Lewis acid-base interactions. This study indicates that ZIF-8 nanocrystals are promising materials for fabricating novel membranes for sewage treatment.