Surface modification of polyether ether ketone implant with a novel nanocomposite coating containing poly (vinylidene...

Polyether ether ketone (PEEK) is an appropriate biomaterial for orthopedic implant applications due to its superior mechanical properties, chemical resistance, nontoxicity, and Magnetic resonance imaging (MRI) compatibility. Unfortunately, the inherent bio-inertness of PEEK restricted its application and required some modification to provide better bioactivity. Besides it, the generated electrical signals in the bone due to its piezoelectricity features have a vital role in regulating bone repair and regeneration. We aimed to modify the surface of PEEK with a dual-functionality nanocomposite that provides surface bioactivity and simulates the piezoelectricity of bone. So, we introduced a novel piezoelectric-bioactive nanocomposite of dispersed poly (vinylidene fluoride) (PVDF) in a sulfonated PEEK (SPEEK) matrix containing Nanohydroxyapatite (nHA) and Carbon nanofiber (CNF) fillers for coating on PEEK substrate to improve its biological activity and simulate the electrical microenvironment for bone tissue. Furthermore, sulfonation of the PEEK surface was conducted as an intermediate layer to prepare better adhesion between the coating nanocomposite and the PEEK sublayer. Surface and cross-section morphology, apatite formation, and cell attachment were investigated on the different treated PEEK surfaces using field-emission scanning electron microscopy (FESEM) and energy dispersive X-ray analysis (EDX). Also, piezoelectric performance, electrical conductivity, contact angle, and mechanical properties were examined on the prepared samples. Moreover, cell viability and cell morphology were investigated for biological evaluation with human osteoblast-like MG-63 cells. Collectively, the hydrophilicity of modified PEEK (mPEEK) coated with nanocomposite was improved due to the synergistic effects of SPEEK functional groups and nHA. Also, comprehensive investigation on the mPEEK treated with nanocomposite indicated a noticeably better bone-like apatite formation, cell proliferation, and cell attachments in the presence of nHA. The transfer of induced piezoelectric charges from dispersed PVDF in the matrix to the surface of nanocomposite containing 2 wt% of CNF increased output voltage to 1893 mV. On the other hand, the presence of CNF in nanocomposites enhanced tensile strength and Young's modulus by 92% and 117%, respectively.