High-pressure synthesis and crystal structures of molybdenum nitride Mo₃N₅ with anisotropic compressibility by a...

A novel high-pressure molybdenum nitride phase, Mo₃N₅, was synthesized at above 45 GPa via a nitridation reaction of molybdenum with nitrogen under high pressure using a laser-heated diamond anvil cell. Mo₃N₅, having an N-N dimer and 7-coordinated Mo sites, crystallizes in an orthorhombic structure with a space group of Cmcm (No. 63) without other prototype structures. The refined lattice parameters for Mo₃N₅ were a = 2.86201(2) Å, b = 7.07401(6) Å, and c = 14.59687(13) Å. The DFT enthalpy calculation suggested that Mo₃N₅ is a high-pressure stable phase, which is also consistent with an increasing coordination number compared to ambient- and low-pressure phases. The zero-pressure bulk modulus of Mo₃N₅ was determined to be K₀ = 328(4) GPa with K'₀ = 10.1(6) by the fitting for the compression curve, which is almost consistent with the theoretical E-V curve and elastic stiffness constants. The compressibility of Mo₃N₅ has axial anisotropy corresponding to the N-N dimer direction in the crystal structure.