A novel all-organic microcapsule with excellent long-term antibacterial and anti-corrosion performances

This work successfully synthesized the salicylic acid@polyurea-formaldehyde (SA@PUF) microcapsules with PUF microcapsules as shell material and SA as core material. The loading content of SA in the PUF microcapsules was approximately 40 %. The SA@PUF microcapsules had excellent long-term antibacterial properties because the PUF microcapsules controlled the release of SA antifouling agents with the ability to induce reactive oxygen species generation and inactivate bacteria. The antibacterial efficiency of SA@PUF microcapsules after 35 days against Staphylococcus aureus and Pseudomonas aeruginosa remained at 80 % and 81 %, increased by 60 % and 62 % compared with pure SA, respectively. The impedance modulus at 0.01 Hz of the SA@PUF coating reached 5.51 GΩ cm², much higher than blank coating (2.55 GΩ cm²) and PUF coating (4.94 GΩ cm²), indicating that the anti-corrosion property of the SA@PUF coating was much better. This work would contribute to developing novel coatings with long-term antibacterial activity and excellent anti-corrosion performance.