The Stabilizing Effect of Carboxymethyl Cellulose on Foamed Concrete

Foam concrete is widely used for its excellent properties, such as light weight, heat insulation, fire resistance, and sound insulation. The stability of foam is the main factor that affects the mechanical performance of foam concrete. The experiments are designed from two perspectives: the foam's stability performance and the foam concrete's modification effect. The effects on foam volume, foam half-life, foam bleeding rate, and foam pore size were investigated based on different concentrations of foam stabilizer CMC (0%, 0.1%, 0.2%, 0.3%, 0.4%, 0.5%). A combination of macroscopic testing and microscopic analysis, a comparative study of dry density, water absorption test, mechanical property test, and pore structure analysis were conducted after using the modified foam for foam concrete. It is shown that the addition of CMC has an enhanced effect on foam stability. Foaming volume, water secretion rate, and average pore size showed a decreasing trend with the increase of CMC admixture, while the foam half-life displayed an increasing trend. In addition, adding CMC reduces the dry density and improves water absorption and compressive strength. The pore structure development of foam concrete has a noticeable improvement effect, and the optimal amount of admixture is 0.4%. Research results provide a reference for applying thickening foam stabilizer CMC in foam concrete.