Full-field Strain Measurements for Microstructurally Small Fatigue Crack Propagation Using Digital Image Correlation Method
07:37

Full-field Strain Measurements for Microstructurally Small Fatigue Crack Propagation Using Digital Image Correlation Method

Published on: January 16, 2019

9.7K

Notch Effects on the Stress Intensity Factor and on the Fatigue Crack Path for Eccentric Circular Internal Cracks in

Jesús Toribio1, Beatriz González1, Juan-Carlos Matos1

  • 1Fracture & Structural Integrity Research Group (FSIRG), University of Salamanca (USAL), E.P.S., Campus Viriato, Avda. Requejo 33, 49022 Zamora, Spain.

Materials (Basel, Switzerland)
|December 23, 2022
PubMed

Keywords:
J-integralconstraint losseccentric circular inner crackelliptical notched barfatigue crack pathfatigue propagationfinite element methodnotch effectstress intensity factor (SIF)

More Related Videos

Crack Monitoring in Resonance Fatigue Testing of Welded Specimens Using Digital Image Correlation05:30

Crack Monitoring in Resonance Fatigue Testing of Welded Specimens Using Digital Image Correlation

Published on: September 29, 2019

8.3K
Ultrasonic Fatigue Testing in the Tension-Compression Mode06:54

Ultrasonic Fatigue Testing in the Tension-Compression Mode

Published on: March 7, 2018

10.8K

Related Concept Videos

Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
223
Relation between Poisson's ratio, Modulus of Elasticity and Modulus of Rigidity01:15

Relation between Poisson's ratio, Modulus of Elasticity and Modulus of Rigidity

Deformation occurs in axial and transverse directions when an axial load is applied to a slender bar. This deformation impacts the cubic element within the bar, transforming it into either a rectangular parallelepiped or a rhombus, contingent on its orientation. This transformation process induces shearing strain. Axial loading elicits both shearing and normal strains. Applying an axial load instigates equal normal and shearing stresses on elements oriented at a 45° angle to the load axis.
313
Stress Concentrations01:24

Stress Concentrations

Stress concentration is when stress intensifies near discontinuities such as holes or abrupt cross-sectional changes in a structural member. This localized stress can often surpass the average stress within the member. The stress distribution in flat bars, either with a circular hole or varying widths connected by fillets, can be determined experimentally using a photoelastic method. The results are based on ratios of geometric parameters like the ratio of the hole's radius to the smaller...
364
Torsion of Noncircular Members01:16

Torsion of Noncircular Members

Circular shafts undergoing torsional stress maintain their cross-sectional integrity due to their axisymmetric nature. This symmetry ensures an even distribution of stress, allowing the shaft to withstand torsion without distorting. In contrast, square bars, lacking this axial symmetry, experience significant distortion across their cross-sections when subjected to torsion, with the exception of along their diagonals and at lines connecting midpoints. A detailed examination of a cubic element...
178
Stress Concentrations in Circular Shafts01:18

Stress Concentrations in Circular Shafts

Consider the elastic torsion formula, which applies to a circular shaft with a consistent cross-section. This formula assumes that the shaft's ends are loaded with rigid plates firmly attached. However, in many cases, torques are applied to the shaft through mechanisms like flange couplings or gears, which are connected by keys inserted into keyways. This application method modifies the stress distribution near the point of torque application, causing it to deviate from the distributions...
224
Stress-Strain Diagram - Ductile Materials01:24

Stress-Strain Diagram - Ductile Materials

The stress-strain relationship in ductile materials such as structural steel or aluminium is intricate and progresses through several stages. When a specimen is loaded, it initially exhibits a linear length increase, depicted by a steep straight line on the stress-strain diagram. It indicates the material is elastically deforming and will return to its original shape once unloaded. However, when a critical stress value is reached, plastic deformation begins. This stage sees substantial...
915