Mechanically Enhanced Nanocrystalline Cellulose/Reduced Graphene Oxide/Polyethylene Glycol Electrically Conductive...

Traditional conductive materials do not meet the increasing requirements of electronic products because of such materials' high rigidity, poor flexibility, and slow biodegradation after disposal. Preparing flexible conductive materials with excellent mechanical properties is an active area of research. The key to flexible conductive materials lies in the combination of the polymer matrix and conductive components. This combination can be achieved by making a film of renewable nano-microcrystalline cellulose (NCC) and reduced graphene oxide (rGO) with excellent electrical conductivity-by simple filtration and introducing polyethylene glycol (PEG) to enhance the functionality of the composite film. Graphene imparted conductivity to the composite film, which reached 5.67 S·m^-1. A reinforced NCC/rGO/PEG-4 composite film with a thickness of only 21 μm exhibited a tensile strength of 30.56 MPa, which was 83% higher than that of the sample without PEG (16.71 MPa), and toughness of 727.18 kJ·m^-3, which was about 132% higher than that of the control sample (NCC/rGO, 313.86 kJ·m^-3). This ultra-thin conductive composite film-which can be prepared simply, consists of environmentally sustainable and biodegradable raw materials, and exhibits excellent mechanical properties-has substantial potential for applications in e.g., flexible electronic wearable devices, electrodes, and capacitors.