Evaluation of the Shape Memory Effect of Random and Aligned Electrospun Polyurethane Mats with Different Fibers...

Fibrous shape memory scaffolds composed of thermoplastic polyurethane based on a mixture of polycaprolactone diols were fabricated. The effect of the fiber diameter and arrangement- random (rPU) or aligned (aPU), on crystallinity, mechanical properties, and shape memory was analyzed. The diameters of the fibers were controlled by changing the concentration of polyurethane (PU) solutions in the range of 5% to 16% and fibers alignment by utilization of different collectors. The chemical structure was confirmed by Fourier Transformed Infrared spectroscopy (FTIR), crystallinity was evaluated based on differential scanning calorimetry (DSC,) and mechanical properties were measured by the tensile test. Additionally, shape memory programming was performed using a dynamic mechanical analyzer (DMA), and shape recovery was evaluated in the air and in the water environment. DSC results showed that the electrospinning process did not change the crystallinity or melting temperature of synthesized thermoplastic polyurethanes. The melting temperature of the crystalline switching segments was around 26-27 °C, and the crystalline phase of hard segments was around 130 °C. Shape memory properties were analyzed in the contest of the fiber diameter and alignment of the fibers, while changes in the fibers' diameters from 360 nm to 1760 nm did not result in significant changes in shape recovery coefficient (Rr) especially evaluated in the air. The longitudinal fiber alignment enhanced mechanical and shape recovery to up to 96% for aPU, with the highest fiber diameter when evaluated in water.