Optimization and Characterization of the F-LSR Manufacturing Process Using Quaternary Ammonium Silanolate as an...

Due to the growing demand for versatile hybrid materials that can withstand harsh conditions (below -40 °C), fluorosilicone copolymers are becoming promising materials that can overcome the limited operating temperature of conventional rubber. In order to synthesize a fluorosilicone copolymer, a potent initiator capable of simultaneously initiating various siloxane monomers in anionic ring-opening polymerization (AROP) is required. In this study, tetramethyl ammonium silanolate (TMAS), a quaternary ammonium (QA) anion, was employed as an initiator for AROP, thereby fluoro-methyl-vinyl-silicone (FVMQ) and fluoro-hydrido-methyl-silicone (FHMQ) were successfully synthesized under optimized conditions. FT-IR, NMR, and GPC analyses confirmed that the chain length and functional group content of FVMQ and FHMQ are controlled by changing the ratio of the components. Moreover, fluorine-involved liquid silicone rubber (F-LSR) was prepared with FVMQ as the main chain and FHMQ as a crosslinker. The tensile strength, elongation, and hardness of each F-LSR sample were measured. Finally, it was confirmed through TGA, DSC, TR-test, and embrittlement testing that elastic retention at low temperatures improved even though the heat resistance slightly decreased as the trifluoropropyl group increased in F-LSR. We anticipate that the optimization of fluorosilicone synthesis initiated by QA and the comprehensive characterization of F-LSRs with different fluorine content and chain lengths will be pivotal to academia and industry.