Diamondlike Carbon Surface Treatment Improves the Fatigue Resistance of Ultrasonic Tips
Emmanuel J N L Silva1, Bruno M Crozeta2, Jorge N R Martins3
1Department of Endodontics, Grande Rio University, Rio de Janeiro, RJ, Brazil; Department of Endodontics, Fluminense Federal University, Niterói, RJ, Brazil; Department of Endodontics, Rio de Janeiro State University, Rio de Janeiro, RJ, Brazil.
Introduction:
The aim of this study was to compare E1-Irrisonic (Helse Ultrasonics, Ocoee, FL) and Irri Black (Helse Ultrasonics), a novel ultrasonic tip with diamondlike carbon treatment, regarding their design, metallurgy, microhardness, bending resistance, and time to fracture under the oscillatory fatigue test.
Methods:
A total of 17 E1-Irrisonic and 17 Irri Black new ultrasonic tips were selected. The tip geometry and surface finishing were assessed using scanning electron microscopy. The elemental composition was defined by energy-dispersive X-ray spectroscopy. Hardness Knoop was calculated using a microhardness tester. The maximum load required to displace the instrument in 45° was recorded in gram/force, oscillatory fatigue was measured in seconds at the moment of instrument fracture, and the size of the separate fragments was determined in millimeters. The Student t test was used for statistical comparison (α = 5%).
Results:
Scanning electron microscopic analyses revealed that E1-Irrisonic had a flat end tip, whereas a noncutting rounded tip was observed in Irri Black. The surface of E1-Irrisonic was smoother than Irri Black, which was irregular. Energy-dispersive X-ray spectroscopic analyses showed that the elemental compositions of the E1-Irrisonic and Irri Black tips were consistent with stainless steel and titanium-aluminum alloys, respectively. Irri Black showed significantly higher bending load resistance, time to fracture under oscillatory motion, and hardness Knoop than the E1-Irrisonic tip (P < .05), whereas the length of fragments was similar (P > .05).
Conclusion:
Diamondlike carbon treatment improved hardness Knoop and reduced the flexibility of the Irri Black ultrasonic tip, improving its time to fracture under oscillatory motion compared with the nontreated E1-Irrisonic tip.