A feasible strategy to balance the performance of stereo-complexed polylactide by incorporating poly(butylene...

The raw material of polylactide (PLA) is lactic acid obtained by biological fermentation. PLA is the most promising degradable polymer to replace traditional plastics to address the pollution problems caused by their non-degradability. However, the application of PLA is hindered by its low softening temperature, easy hydrolysis, and poor toughness. Herein, the ternary composites with PLLA, PDLA and Poly (butylene adipate-co-terephthalate) (PBAT) were prepared by melt blending to balance its thermal stability, hydrolysis, and toughness. The effects of PBAT content (3 %, 6 %, 9 % and 12 %) and isothermal crystallization temperature on composite properties were fully investigated. The results show that the composite of stereo-complexed PLA (sc-PLA) with 6 % PBAT crystallized at 110 °C exhibits good comprehensive properties. Its vicat softening temperature (VST), mass loss rate under alkaline (pH = 12) and breaking elongation are 166 °C, 21.6 % and 4.40 %, respectively. Compared with the pure PLLA sample crystallized at same condition, the VST, mass loss rate and breaking elongation are 159 °C, 24.7 % and 3.76 % respectively, which increased by nearly 5 %, 13 % and 20 %. This indicates that this strategy is feasible to balance the heat resistance, hydrolysis resistance and toughness of PLA, while it sacrifices the tensile strength a little. This work provides a new way to modify and improve the PLA properties. Nonetheless, it is also necessary to coordinate the compatibility of PLA and PBAT.