Polypyrrole-Coated Low-Crystallinity Iron Oxide Grown on Carbon Cloth Enabling Enhanced Electrochemical...

It is highly attractive to design pseudocapacitive metal oxides as anodes for supercapacitors (SCs). However, as they have poor conductivity and lack active sites, they generally exhibit an unsatisfied capacitance under high current density. Herein, polypyrrole-coated low-crystallinity Fe₂O₃ supported on carbon cloth (D-Fe₂O₃@PPy/CC) was prepared by chemical reduction and electrodeposition methods. The low-crystallinity Fe₂O₃ nanorod achieved using a NaBH₄ treatment offered more active sites and enhanced the Faradaic reaction in surface or near-surface regions. The construction of a PPy layer gave more charge storage at the Fe₂O₃/PPy interface, favoring the limitation of the volume effect derived from Na⁺ transfer in the bulk phase. Consequently, D-Fe₂O₃@PPy/CC displayed enhanced capacitance and stability. In 1 M Na₂SO₄, it showed a specific capacitance of 615 mF cm^-2 (640 F g^-1) at 1 mA cm^-2 and still retained 79.3% of its initial capacitance at 10 mA cm^-2 after 5000 cycles. The design of low-crystallinity metal oxides and polymer nanocomposites is expected to be widely applicable for the development of state-of-the-art electrodes, thus opening new avenues for energy storage.