Dentin primer based on a highly functionalized gelatin-methacryloyl hydrogel

Gelatin-methacryloyl hydrogels (GelMA) have demonstrated their utility as scaffolds in a variety of tissue engineering applications.

In this study, a highly functionalized GelMA hydrogel was synthesized and assessed for degree of functionalization. As the proposed GelMA hydrogel was coupled to a visible-light photoinitiator, we hypothesized it might serve as base to formulate a model dentin primer for application in restorative dentistry.

GelMA was mixed with photoinitiator lithium phenyl-2,4,6-trimethylbenzoylphosphinate (LAP), photopolymerized for 0-40 s using a dental light-curing device and tested for extrudability, degree of photo-crosslinking (DPxlink), water sorption/solubility/swelling (WS/SL/SW) and apparent modulus of elasticity (AE). Model dentin primer was prepared by mixing GelMA+LAP with a primer of a commercial three-step etch-and-rinse adhesive. After application of GelMA-based primer to acid-etched dentin, samples were bonded with correspondent adhesive agent, photopolymerized and had their immediate bond strength compared to control samples primed and bonded with the same commercial material.

Extrudability of hydrogel was confirmed using a microsyringe to write the acronym "CDMI". DPxlink of GelMA+LAP changed significantly as a function of photopolymerization time (20 s < 30 s ≤ 40 s). WS, SL and SW were significantly reduced in hydrogels polymerized for 30 and 40 s. AE of hydrogels varied significantly as a function of photopolymerization time (20 s < 30 s ≤ 40 s; 20 s ‡ 40 s). Bond strength of dentin primed with GelMA-based primer was lower (∼29.3 MPa) but not significantly of that of control (∼34.6 MPa).

Optimization of a GelMA-based dentin primers can lead to the development of promising biomimetic adhesives for dentin rehabilitation.