Surface analysis and thermal behavior of the functionalized cellulose by glutaric anhydride through a solvent-free...

According to the 12 principles of green chemistry, surface functionalization was performed using glutaric anhydride under solvent-free and catalyst-free conditions. FTIR spectra and DS analyses demonstrated the functionalization of HCl-hydrolyzed cellulose. The influence of two parameters, i.e., the glutaric anhydride concentration and the reaction time, on the functionalization of HCl-hydrolyzed cellulose was investigated. Protocol efficiency was studied by a degree of substitution (DS). It was found that higher concentrations of glutaric anhydride cause an enhancement of DS to 0.75 and 0.87 for GA3-12 and GA9-12, respectively. In addition, the longer reaction time increased zeta potential from -12.2 ± 1.7 for G9-6 to -34.57 ± 2.2 for GA9-12. Morphology analysis by SEM showed a decrease in fiber length for the functionalized cellulose. DSC profiles confirmed dehydration at a range of 17 to 134 °C. A glass transition was revealed at -30 to -20 °C for all studied samples. The fusion, the depolymerization of cellulose chains, the cleavage of glycosidic linkages, and the decomposition of the crystalline parts of cellulose occur at 195 to 374 °C. Therefore, an efficient and greener process was developed to functionalize the HCl-hydrolyzed cellulose by glutaric anhydride, a safe and non-toxic anhydride, in the absence of the solvent and catalyst.