Tuning of Optical Stopband Wavelength and Effective Bandwidth of Gel-Immobilized Colloidal Photonic Crystal Films

We show that both the optical stopband wavelength and effective bandwidth of films of gel-immobilized loosely packed colloidal photonic crystals can be controlled over a wide range. When the gelation reagent of the charge-stabilized colloidal crystals was photopolymerized under ultraviolet light using different upper- and bottom-light intensities, it resulted in a gel-immobilized colloidal crystal film with a broadened Bragg reflection peak. Moreover, the width of the Bragg peak increased from 30 to 190 nm as the difference between the light intensities increased. Films with wider Bragg peaks exhibited a brighter reflection color because of the superposition of the shifted Bragg reflections. Furthermore, the Bragg wavelength could be varied over a wide range (500-650 nm) while maintaining the same broadened effective bandwidth by varying the swelling solvent concentration. These findings will expand the applicability of colloidal crystals for use in photonic devices and color pigments.