Experimental and Theoretical Tests on the Corrosion Protection of Mild Steel in Hydrochloric Acid Environment by the

Maria Boudalia1,2, R M Fernández-Domene2,3, L Guo4

  • 1Laboratory of Materials, Nanotechnology and Environment, Faculty of Sciences, Mohammed V University in Rabat, P.O. Box 1014, Rabat 10090, Morocco.

Materials (Basel, Switzerland)
|January 21, 2023
PubMed

Keywords:
Monte Carlo simulationcorrosion inhibitordensity functional theoryelectrochemistryweight loss

More Related Videos

Potentiodynamic Corrosion Testing08:43

Potentiodynamic Corrosion Testing

Published on: September 4, 2016

17.7K
The Evolution of Silica Nanoparticle-polyester Coatings on Surfaces Exposed to Sunlight10:27

The Evolution of Silica Nanoparticle-polyester Coatings on Surfaces Exposed to Sunlight

Published on: October 11, 2016

9.6K

Related Concept Videos

Corrosion of Reinforcement01:27

Corrosion of Reinforcement

The corrosion of steel reinforcement within concrete is a process influenced by the material's inherent properties and external factors. The high pH level of around 13, provided by calcium hydroxide present in concrete, initially protects the steel reinforcement by promoting the formation of a passive iron oxide layer on its surface.
However, over time and under certain conditions like carbonation, chloride ingress, and cracking this protective state can be compromised. Steel has areas with...
230
Corrosion02:49

Corrosion

The degradation of metals due to natural electrochemical processes is known as corrosion. Rust formation on iron, tarnishing of silver, and the blue-green patina that develops on copper are examples of corrosion. Corrosion involves the oxidation of metals. Sometimes it is protective, such as the oxidation of copper or aluminum, wherein a protective layer of metal oxide or its derivatives forms on the surface, protecting the underlying metal from further oxidation. In other cases, corrosion is...
25.4K
Acid Halides to Carboxylic Acids: Hydrolysis01:01

Acid Halides to Carboxylic Acids: Hydrolysis

Hydrolysis of acid halides is a nucleophilic acyl substitution reaction in which acid halides react with water to give carboxylic acids. The reaction occurs readily and does not require acid or a base catalyst.
As shown below, the mechanism involves a nucleophilic attack by water at the carbonyl carbon to form a tetrahedral intermediate. This is followed by the reformation of the carbon–oxygen π bond along with the departure of a halide ion. A final proton transfer step yields carboxylic...
2.8K
Acid Attack on Concrete01:21

Acid Attack on Concrete

When acids come into contact with concrete, they initiate a chemical reaction that dissolves the hydrated cement paste. This process leads to softening and structural weakening of the concrete. This issue is commonly observed in environments such as chimneys, sewers, and industrial settings. The severity of the damage increases as the pH of the water interacting with the concrete drops below 6.5. In particular, a pH under 4.5 can cause significant concrete damage.
The rate at which hydrogen...
298
Acid Halides to Esters: Alcoholysis01:12

Acid Halides to Esters: Alcoholysis

Alcoholysis is a nucleophilic acyl substitution reaction in which an alcohol functions as a nucleophile. Acid halides react with alcohol to produce esters. The mechanism proceeds in three steps:
3.0K
Diazonium Group Substitution: –OH and –H01:19

Diazonium Group Substitution: –OH and –H

Nitrous acid, a weak acid, is prepared in situ via the reaction of sodium nitrite with a strong acid under cold conditions. This nitrous acid prepared in situ reacts with primary arylamines to form arenediazonium salts. Such reactions are known as diazotization reactions. As shown in Figure 1, the formation of arenediazonium salts begins with the decomposition of nitrous acid in an acidic solution to give nitrosonium ions.
2.9K