Improvements in Temperature Uniformity in Carbon Fiber Composites during Microwave-Curing Processes via a Recently...

Curing processes for carbon-fiber-reinforced polymer composites via microwave heating are promising alternatives to conventional thermal curing because this technology results in nonhomogeneous temperature distributions, which hinder its further development in industries. This paper proposes a novel method for improving heating homogeneities by employing three-dimensional motion with respect to the prepreg laminate used in the microwave field by using a recently developed microwave system. The maximum temperature deviation on the surface of the laminate can be controlled within 8.7 °C during the entire curing process, and it produces an average heating rate of 1.42 °C/min. The FT-IR analyses indicate that microwave heating would slightly influence hydroxyl and methylene contents in the cured laminate. The DMA measurements demonstrate that the glass transition temperatures can be improved by applying proper microwave-curing processes. Optical microscopy and mechanical tests reveal that curing the prepreg laminate by using a multistep curing process that initially cures the laminate at the resin's lowest viscosity for 10 min followed by curing the laminate at a high temperature for a short period of time would be favorable for yielding a sample with low void contents and the desired mechanical properties. All these analyses are supposed to prove the feasibility of controlling the temperature difference during microwave-curing processes within a reasonable range and provide a cured laminate with improved properties compared with conventional thermally cured products.