Functionalized agarose hydrogel with in situ Ag nanoparticles as highly recyclable heterogeneous catalyst for...

In the present research work, a highly recyclable catalyst of Ag-based agarose (HRC-Ag/Agar) hydrogel was successfully fabricated through a simple and efficient in situ reduction method without the aid of additional surface active agent. The interaction between the rich hydroxyl functional (-OH) groups in agarose and Ag can effectively control the growth and dispersion of Ag nanoparticles (NPs) in the HRC-Ag/Agar hydrogel and keep Ag NPs free from chemical contamination, which also guarantees the reusability of HRC-Ag/Agar hydrogel as catalysts. HRC-Ag/Agar hydrogel without freeze drying and calcination was investigated for their potential applications as highly active/recyclable catalysts in reducing aromatic organic pollutants (p-nitrophenol (4-NP), methylene blue (MB) and rhodamine B (RhB)) by KBH₄. The optimal HRC-Ag/Agar-1.9 hydrogel can complete the catalytic reduction of 4-NP within 11 min. Moreover, HRC-Ag/Agar-1.9 hydrogel achieves the high conversion rate (> 99%) through ten catalytic runs. Similarly, HRC-Ag/Agar-1.9 hydrogel was able to achieve a reduction efficiency of RhB at 98% within 17 min and that of MB at 95% within 40 min. The advantages of simple synthetic procedure, no secondary pollution, strong stability and easily separated make the HRC-Ag/Agar hydrogel have great potential prospect for environmental applications.