Fracture Gap Closure and Reduction Are Affected by the Orientation of the Headless Compression Screw

We evaluated the impact of a variable-pitch headless screw's angle of insertion relative to the fracture plane on fracture gap closure and reduction.

Variable-pitch, fully threaded headless screws were inserted into polyurethane blocks of "normal" bone model density using a custom jig. Separate trials were completed with a 28-mm screw placed perpendicular and oblique/longitudinal to varying fracture planes (0°, 15°, 30°, 45°, and 60°). Fluoroscopic images were taken after each turn during screw insertion and analyzed. Initial screw push-off, residual fracture gap at optimal fracture gap reduction, and malreduction were determined in each trial. Statistical analysis was performed via a 1-way analysis of variance followed by Student t tests.

Malreduction was found to be significantly different between the perpendicular (1.88 mm ± 1.38) and the oblique/longitudinal (0.58 mm ± 0.23) screws. The malreduction increased for the perpendicular screw as the fracture angle increased (60° > 45°=30° > 15° > 0°). Residual fracture gap at optimal fracture gap reduction was also found to be significantly different between the perpendicular (0.97 ± 0.42) and oblique/longitudinal (1.43 ± 1.14) screws. The residual fracture gap increased for the oblique/longitudinal screw as the fracture angle increased, although the oblique/longitudinal screw with a 60° fracture angle was the only configuration significantly larger than all the other configurations. Screw push-off was not found to be significantly different between the oblique/longitudinal screw and perpendicular screw trials.

The perpendicular screw had a larger malreduction that increased with fracture angle, whereas the oblique/longitudinal screw had a larger residual fracture gap that increased with fracture angle.