Enhanced Energy Storage Properties in Lead-Free (Na_0.5Bi_0.5)_0.7Sr_0.3TiO₃-Based Relaxor Ferroelectric Ceramics through...

Although relaxor ferroelectrics have been widely investigated owing to their various advantages, there are still impediments to boosting their energy-storage density (W_rec) and energy-storage efficiency (η). In this paper, we propose a cooperative optimization strategy for achieving comprehensive outstanding energy-storage performance in (Na_0.5Bi_0.5)_0.7Sr_0.3TiO₃ (NBST)-based ceramics by triggering a nonergodic-to-ergodic transformation and optimizing the forming process. The first step of substituting NaNbO₃ (NN) for NBST generated an ergodic state and induced polar nanoregions under the guidance of a phase-field simulation. The second step was to apply a viscous polymer process (VPP) to the 0.85NBST-0.15NN ceramics, which reduced porosity and increased compactness, resulting in a significant polarization difference and high breakdown strength. Consequently, 0.85NBST-0.15NN-VPP ceramics optimized by this cooperative two-step strategy possessed improved energy-storage characteristics (W_rec = 7.6 J/cm³, η = 90%) under 410 kV/cm as well as reliable temperature adaptability within a range of 20-120 °C, outperforming most reported (Na_0.5Bi_0.5) TiO₃-based ceramics. The improved energy-storage performance validates the developed ceramics' practical applicability as well as the advantages of implementing a cooperative optimization technique to fabricate similar high-performance dielectric ceramics.