Synthesis of nickel nanowires (Ni-NWs) as high ferromagnetic material by electrodeposition technique

Metallic nanowires (NWs) and their different compounds display incredible prospects for their use in various applications including media storage, sensor and solar cell devices along with the biological drug delivery systems. In this research work, the metallic NWs like nickel nanowires (Ni-NWs) are synthesized successfully by employing electrodeposition process. Anodic aluminum oxide (AAO) templates are employed as a platform with copper metal coating which acts as an active cathode. The synthesized Ni-NWs are examined through various characterization techniques including X-ray diffraction (XRD), scanning electron microscope (SEM) and vibrating sample magnetometer (VSM) to study the crystal structure, surface morphology and magnetic properties, respectively. The XRD analysis shows the development of various diffraction planes like Ni (111), Ni (200), Ni (220) which confirms the formation of polycrystalline nickel NWs. The SEM analysis reveals that the range of diameter and length of nickel NWs are found to be ∼160 to 200 and ∼4 to 11 micron respectively showing high aspect ratio (ranged from ∼200 to 300). The ferromagnetic behavior of Ni-NWs is confirmed by the hysteresis loop carried out for parallel and perpendicular configurations having H_c = 100 and 206 Oe, respectively. The obtained results suggest that the synthesized Ni- NWs may be used for high-density media storage devices.