Cyclic and Torsional Fatigue Resistance of Seven Rotary Systems

Renan D Furlan1, Murilo P Alcalde1, Marco A H Duarte1

  • 1School of Dentistry, University of São Paulo, 17012-901 Bauru, SP, Brazil.

Iranian Endodontic Journal
|January 27, 2023
PubMed
Abstract

Keywords:
Cyclic FatigueRoot Canal PreparationTorsional Fatigue

More Related Videos

Scanning Electron Microscopic Evaluation of Surface Defects of Remover Retreatment File After Single and Multiple Uses03:07

Scanning Electron Microscopic Evaluation of Surface Defects of Remover Retreatment File After Single and Multiple Uses

Published on: October 11, 2024

579
Author Spotlight: Integrating Mechanical and Biological Analysis in Tendinopathy Research04:37

Author Spotlight: Integrating Mechanical and Biological Analysis in Tendinopathy Research

Published on: March 1, 2024

918

Related Concept Videos

Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
222
Deformation in a Circular Shaft01:10

Deformation in a Circular Shaft

One of the distinctive characteristics of circular shafts is their ability to maintain their cross-sectional integrity under torsion. In other words, each cross-section continues to exist as a flat, unaltered entity, simply rotating like a solid, rigid slab. To understand the distribution of shearing stress within such a shaft, consider a cylindrical section inside this circular shaft. This section has a length of L and a radius of R, with one end fixed. The radius of the cylindrical section is...
409
Stress Concentrations in Circular Shafts01:18

Stress Concentrations in Circular Shafts

Consider the elastic torsion formula, which applies to a circular shaft with a consistent cross-section. This formula assumes that the shaft's ends are loaded with rigid plates firmly attached. However, in many cases, torques are applied to the shaft through mechanisms like flange couplings or gears, which are connected by keys inserted into keyways. This application method modifies the stress distribution near the point of torque application, causing it to deviate from the distributions...
220
Thin-Walled Hollow Shafts01:15

Thin-Walled Hollow Shafts

In analyzing a thin-walled hollow shaft subjected to torsional loading, a segment with width dx is isolated for examination. Despite its equilibrium state, this segment faces torsional shearing forces at its ends. These forces are quantitatively described by the product of the longitudinal shearing stress on the segment's minor surface and the area of this surface, leading to the concept of shear flow. This shear flow is consistent throughout the structure, indicating a uniform distribution...
223
Torsion of Noncircular Members01:16

Torsion of Noncircular Members

Circular shafts undergoing torsional stress maintain their cross-sectional integrity due to their axisymmetric nature. This symmetry ensures an even distribution of stress, allowing the shaft to withstand torsion without distorting. In contrast, square bars, lacking this axial symmetry, experience significant distortion across their cross-sections when subjected to torsion, with the exception of along their diagonals and at lines connecting midpoints. A detailed examination of a cubic element...
177
Residual Stresses in Circular Shafts01:10

Residual Stresses in Circular Shafts

In materials that exhibit elastic and plastic behavior, known as elastoplastic materials, residual stresses can accumulate when these materials experience plastic deformation. This deformation arises from either high levels of shearing stress or significant strains. Residual stresses are internal stresses that persist within a material after removing the external force causing deformation. This phenomenon is demonstrated when observing the behavior of a shaft under torque; notably, the...
216