Toward ultra-tough and heat-resistant biodegradable polylactide/core-shell rubber blends by regulating the...

Ultra-tough and heat-resistant poly(l-lactide)/core-shell rubber (PLLA/CSR) blends were fabricated by utilizing stereocomplex (SC) crystallites to effectively regulate the CSR distribution in PLLA matrix. Linear and 3-11 armed poly(d-lactide)s (PDLAs) were synthesized and then melt-mixed with PLLA/CSR blend. Interestingly, the incorporated PDLA chains could collaborate with PLLA chains to form dense SC crystallites network in PLLA/PDLA/CSR blends, thus inducing the CSR particles to transform from uniform distribution structure to network-like structure. With increasing the PDLA arm numbers, the size of CSR clusters in the network-like structure first increased and then decreased, and the continuity of the network-like structure first remained at a high level and then decreased obviously. The formation of CSR network-like structure could remarkably improve the impact strength of PLLA/PDLA/CSR blends without deteriorating their strength and modulus (compared with PLLA/CSR blend), and the CSR network-like structure with larger-sized CSR clusters and higher continuity could help obtain higher impact strength (78.3 kJ/m²). Moreover, the heat resistance of PLLA/PDLA/CSR blends could also be significantly improved (the highest Vicat softening temperature was 131 °C) by the SC crystallites network and CSR network-like structure. This work provides an effective strategy for controlling the rubber network-like morphology and thereby preparing high-performance PLLA materials.