First-principles calculations of Mg₂FeH₆ under high pressures and hydrogen storage properties

We report on structural properties, elastic constants, mechanical and dynamical stabilities, electronic band structure, and hydrogen storage applications of Mg₂FeH₆ at zero and high-pressure effects. The work has been realized within the full-potential linearized augmented plane wave method. At zero pressure, the material under study is stable and has a ductile nature. The electronic structure of the material of interest is determined to be X-X wide direct band gap semiconductor with an energy of 1.88 eV. The hydrogen storage capacity wt (%) and the hydrogen desorption temperature are reported as 5.473 and 625.47 K respectively. The Debye temperature ϴ_D is recorded as 698 K using the elastic constants and about 775 K using the Gibbs calculations. Under high-pressure effect up to 80 GPa, the semiconductor still be an X-X semiconductor with an energy gap of 3.91 eV. The Debye temperature ϴ_D increases monotonically up to about 1120 K at 80 GPa when using the calculated elastic constants whereas the desorption temperature decreases from 650 to 0 K by increasing pressure from 0 to about 87 GPa.