Effect of crystal orientation on flexural strength of pressable lithium disilicate glass-ceramics

This study examined the crystal orientation of four kinds of pressable lithium disilicate glass-ceramics and evaluated the effect of crystal orientation on flexural strength. Bar-shaped (24 mm in length, 1.2 mm in thickness, 4.0 mm in width), disk-shaped (12 mm in diameter, 0.5 mm in thickness), and crown-shaped (maxillary first molar) specimens were prepared according to the manufacturer's instructions. Three-point and biaxial flexural strengths were measured for bar- and disk-shaped specimens. Microstructure analysis was performed using X-ray diffractometry and scanning electron microscopy. Three-point flexural strength was improved by parallel crystal orientation along the longitudinal direction of the bar-shaped specimen. There was no relationship between two-dimensional crystal orientation and biaxial flexural strength. The results of this study assumed that biaxial flexural strength was improved by the crystal orientation in the cross-sectional direction. Pressed restorations are expected to possess higher strength than milled restorations due to their crystal orientation.