Biocompatibility and osteointegration capability of β-TCP manufactured by stereolithography 3D printing: In vitro...

Beta-tricalcium phosphate (β-TCP) bioceramics have an inorganic composition similar to the human bone. While conventional methods can only produce ceramic scaffolds with poor controllability, the advancement of 3D-printing, especially stereolithography, made it possible to manufacture controllable, highly precise, micropore ceramic scaffolds. In this study, the stereolithography was applied to produce β-TCP bioceramics, while ZrO₂, Al₂O₃, Ti6Al4V, and polyetheretherketone (PEEK) were used as controls. Phase analysis, water contact angle tests, and Micro-CT were applied to evaluate the surface properties and scaffold. Hemolytic toxicity, cell proliferation, and morphological assessment were performed to evaluate the biocompatibility. Alkaline phosphatase (ALP) level, mineralization, and qRT-PCR were measured to evaluate the osteointegration. During the manufacturing of β-TCP, no evident impurity substance and hemolytic toxicity was found. Cells on β-TCP had good morphologies, and their proliferation capability was similar to Ti6Al4V, which was higher than the other materials. Cells on β-TCP had higher ALP levels than PEEK. The degree of mineralization was significantly higher on β-TCP. The expression of osteogenesis-related genes on β-TCP was similar to Ti6Al4V and higher than the other materials. In this study, the β-TCP produced by stereolithography had no toxicity, high accuracy, and excellent osteointegration capability, thus resulting as a good choice for bone implants.